GB Cr12MoV | DIN 1.2601 | ASTM D5 Cold Work Tool Steel
Port: Hu nan
Supply Ability: 10000 Ton/Tons per Year
Min.Order Quantity: 15 Ton/Tons
Your present location:Home > Products > Cold Work Tool Steel
-
Quick Details
1: DIN 1.2601 steel introduction
DIN 1.2601 is a Cold work tool alloy steel material grade.it is shock resisting steel. Digital Grade material number 1.2601 use in extrusion moulds, Hot Cast moulds. like aluminium production, Aluminium cutting mold. Our Tool Steel material 100 % ultrasonic tested with good price. Small size steel products make by hot rolled, large size steel products make by forging. 1.2601 with is equivalent Belong to DIN.
2: DIN 1.2601 steel equivalent
Country
China Japan Germany USA UK Standard
GB/T 1299
JIS G4404
DIN EN ISO4957
ASTM A681
BS 4659
Grade
Cr12MoV
1.2601
D5
3: DIN 1.2601 steel chemical composition
Grade C Mn P S Si W V Cr DIN 1.2601 1.55 1.75 0.20 0.40 0.03 0.03 0.25 0.40 0.40 0.6. 0.1 0.50 11.0 12.0
4: DIN 1.2601 steel mechanical properties
Grade
Tensile strength
Yield strength
Elongation
Reduction
Impact Value
Hardness
DIN 1.2601
488 (≥)MPa
12%
31%
31J
Annealing 225 HB max, Q+T: 58-63 HRc
5: DIN 1.2601 steel overviewsSize Round Dia 6-1200mm Plate/Flat/Block Thickness
6mm-500mmWidth
20mm-1000mmProcess EAF+LF+VD+Forged+Heat treatment(optional) Heat treatment Normalized ; Annealed ; Quenched ; Tempered Surface condition Black; Peeled; Polished; Machined; Grinded; Turned; Milled Delivery condition Forged; Hot rolled; Cold drawn Test Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. Payment terms T/T;L/C;/Money gram/ Paypal Trade terms FOB; CIF; C&F; etc.. Packing Standard Packages, or as Customers Request
Delivery time 30-45 days Application DIN 1.2601 is suitable for applications High alloyed CrMoV steel for cutting tool and cold work tool steel.
6:Heat treatment
Annealing:
Temperature/℃: 800~830; After the annealing, degree of hardness ≤HBS: 255
Quenching:
Hardening temperature/℃: 980~1010, Quenching in oil or air
Tempering:
Commonly used drawing temperature/℃: 180~250; After tempering hardness HRC | 100 ℃ : 63; After tempering hardness HRC | 200 ℃ : 61; After tempering hardness HRC | 300 ℃ : 60 ; After tempering hardness HRC | 400 ℃ : 58
Normalizing
at Normalizing temperature, then cool in furnace
7: Delivery condition
For hot forged or hot rolled bar, usually the delivery condition is hot forged or rolled, annealed, rough turned.
For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface.
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.