1: 1.2885 steel introduction
German DIN 1.2885 steel is a high life chromium-molybdenum-vanadium hot working alloy tool box with uniform machinability and good heat treatment characteristics. It has excellent temper softening resistance, unique thermal fatigue resistance and excellent thermal conductivity, longitudinal and transverse toughness and ductility.
2: 1.2885 steel equivalent
|
Country
|
China
|
Japan
|
Germany
|
USA
|
|
Standard
|
GB/T
|
JIS
|
DIN (W-Nr.)
|
AISI/ASTM
|
|
Grade
|
|
|
X32CrMoCoV3-3-3
|
H10A
|
3: 1.2885 steel chemical composition
|
Grade
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
|
V
|
|
X32CrMoCoV3-3-3
|
0.28-0.35
|
0.10-0.40
|
0.15-0.45
|
0.03
|
0.03
|
2.70-3.20
|
2.60-3.00
|
0.40-0.70
|
4: 1.2885 steel mechanical properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
5: 1.2885 steel overviews
|
Size
|
Round
|
Dia 6-1200mm
|
|
Plate/Flat/Block
|
Thickness
6mm-500mm
|
Width
20mm-1000mm
|
|
Heat treatment
|
Normalized ; Annealed ; Quenched ; Tempered
|
|
Surface condition
|
Black; Peeled; Polished; Machined; Grinded; Turned; Milled
|
|
Delivery condition
|
Forged; Hot rolled; Cold drawn
|
|
Test
|
Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc.
|
|
Payment terms
|
T/T;L/C;/Money gram/ Paypal
|
|
Trade terms
|
FOB; CIF; C&F; etc..
|
|
Delivery time
|
30-45 days
|
|
Application
|
1.2885 Steel is used for hot pressing tools to withstand severe stresses when in contact with die inserts-mandrels, seals, stamping tools, dies, etc.
|
6: Heat Treatment
Heat treatment temperatures, rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, the quenching medium and work piece transfer facilities. Please consult a heat treatment specialist for full guidance on heat treatment.
7: Delivery condition
For hot forged bar, usually the delivery condition is hot forged, annealed/QT, rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed/QT, Black surface.
For hot forged block, usually the delivery condition is hot forged, annealed/QT, milled surface/Black surface
For hot rolled plate, usually the delivery condition is hot rolled, annealed/QT, black surface.
For cold drawn bar, usually the delivery condition is cold drawn, annealed/QT, peeled/black surface